Celstran® PA66-GF50-02P11/14
聚酰胺66
Ticona
Technical Data
产品说明
Material code according to ISO 1043-1: PA66
Heat stabilized Nylon 66 reinforced by 50 weight percent long glass fibers. The pellets are cylindrical and normally as well as the embedded fibers 11 mm long.
Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly.
The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding.
Can be used for substituting die cast metal with the advantage of Weight reduction, no corrosion problems, no post treatment.
总体
材料状态 • 已商用：当前有效
资料 1 • Technical Datasheet (English)
• Processing - Injection (English)
Search for UL Yellow Card • Ticona
• Celstran®
供货地区 • 欧洲
填料/增强材料 • 长玻璃纤维, 50% 填料按重量
添加剂 • 热稳定剂
性能特点 • 低翘曲性 • 高强度 • 热稳定性
• 刚性，高 • 耐热性，高
用途 • 金属置换
RoHS 合规性 • 联系制造商
加工方法 • 片材挤出成型 • 注射成型
树脂ID (ISO 1043) • PA66
物理性能 额定值 单位制 测试方法
密度 1.57g/cm³ ISO 1183
粘数 136cm³/g ISO 307
机械性能 额定值 单位制 测试方法
拉伸模量
-- 16800MPa ISO 527-2/1A/1
80°C 10000MPa ISO 527-2
拉伸应力
断裂 220MPa ISO 527-2/1A/5
80°C 140MPa ISO 527-2
拉伸应变
断裂 1.6% ISO 527-2/1A/5
断裂, 80°C 1.8% ISO 527-2
弯曲模量 ISO 178
23°C 15500MPa
80°C 10500MPa
弯曲强度 ISO 178
23°C 330MPa
80°C 260MPa
1 / 3
Celstran® PA66-GF50-02P11/14
聚酰胺66
Ticona
冲击性能 额定值 单位制 测试方法
简支梁缺口冲击强度 ISO 179/1eA
-30°C 30kJ/m²
23°C 30kJ/m²
简支梁缺口冲击强度 ISO 179/1eU
-30°C 58kJ/m²
23°C 60kJ/m²
无缺口伊佐德冲击强度 ISO 180/1U
-30°C 47kJ/m²
23°C 54kJ/m²
多轴向仪器化冲击能量 (-30°C) 23.8J ISO 6603-2
热性能 额定值 单位制 测试方法
热变形温度
1.8 MPa, 未退火 258°C ISO 75-2/A
8.0 MPa, 未退火 240°C ISO 75-2/C
熔融温度 3 260°C ISO 11357-3
注射 额定值 单位制
加工（熔体）温度 310 到 325°C
模具温度 90.0 到 120°C
注射说明
During the processing of CELSTRAN it is important to watch and
control melt shear, for excessive shear reduces fiber length and
mechanical performance as well.
Processing recommendation:
• Conventional 3 zone screw, screw diameter minimum 40 mm
• Design flow channels for low melt shear
• Back pressure and screw rotation to realize a continous plastification performance and thus a homogeneous melt.
• Apply higher temperature settings than for short fiber compounds
备注
1 通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。
2 一般属性：这些不能被视为规格。
3 10°C/min
|