Celstran® PA66-GF50-20 AD3007
聚酰胺66
Ticona i
Technical Data
产品说明
Material code according to ISO 1043-1: PA66
Heat stabilized Nylon 66 reinforced by 50 weight percent long glass fibers. The pellets are cylindrical and normally as well as the embedded fibers 11 mm long.
Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly.
The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding.
Can be used for substituting die cast metal with the advantage of Weight reduction, no corrosion problems, no post treatment.
总体
材料状态 • 已商用：当前有效
资料 1 • Technical Datasheet (English)
• Processing - Injection (English)
Search for UL Yellow Card • Ticona
• Celstran®
供货地区 • 北美洲 • 欧洲
填料/增强材料 • 玻璃纤维增强材料, 50% 填料按重量
添加剂 • 热稳定剂
性能特点 • 低翘曲性 • 高强度 • 耐低温撞击
• 刚性，高 • 抗撞击性，高 • 热稳定性
用途 • 金属置换
RoHS 合规性 • 联系制造商
加工方法 • 注射成型
树脂ID (ISO 1043) • PA66
物理性能 额定值 单位制 测试方法
密度 1.57g/cm³ ISO 1183
粘数 132cm³/g ISO 307
机械性能 额定值 单位制 测试方法
拉伸模量
-- 16500MPa ISO 527-2/1A/1
80°C 10000MPa ISO 527-2
拉伸应力
断裂 250MPa ISO 527-2/1A/5
80°C 165MPa ISO 527-2
拉伸应变
断裂 2.0% ISO 527-2/1A/5
断裂, 80°C 2.7% ISO 527-2
弯曲模量 ISO 178
23°C 14200MPa
80°C 10000MPa
弯曲强度 ISO 178
23°C 400MPa
80°C 265MPa
1 / 3
Celstran® PA66-GF50-20 AD3007
聚酰胺66
Ticona
冲击性能 额定值 单位制 测试方法
简支梁缺口冲击强度 ISO 179/1eA
-30°C 45kJ/m²
23°C 45kJ/m²
简支梁缺口冲击强度 ISO 179/1eU
-30°C 78kJ/m²
23°C 87kJ/m²
热性能 额定值 单位制 测试方法
热变形温度
1.8 MPa, 未退火 255°C ISO 75-2/A
8.0 MPa, 未退火 235°C ISO 75-2/C
熔融温度 3 260°C ISO 11357-3
备注
1 通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。
2 一般属性：这些不能被视为规格。
3 10°C/min
|