13549213581肖生

FDA食品级，良好耐磨损性, 韧性良好, 高强度, 抗溶剂性, 衬套, 电器外壳, 连接器, 凸轮, 轴承

 

Vydyne® 21SPF

聚酰胺66

Ascend Performance Materials Operations LLC

Technical Data

 

产品说明

 

Vydyne 21SPF is a general-purpose PA66 resin. Available in natural, it is designed principally for injection-molding fabrication. This grades offer a well-balanced combination of engineering properties characterized by high strength; rigidity; good toughness; high melt point; good surface lubricity; abrasion resistance and resistance to many chemicals, machine and motor oils, solvents and gasoline.

 

Vydyne 21SPF resin permits production of molded parts with good initial color plus good property and color retention when using regrind. This resin is recognized by Underwriters Laboratories and conforms to the requirements of many industrial, federal and military specifications for premium-quality, general-purpose PA66 resins.

 

Vydyne 21SPF resin is internally and externally lubricated for improved machine feed and exceptional mold release. It is intended for use in high-productivity applications. In many applications, the molding cycle can be reduced because parts may be removed from the cavity at higher temperatures. In difficult molds where parts have a tendency to stick in the cavity, Vydyne 21SPF can reduce or eliminate the need for mold release sprays. Critical molded part dimensions should be checked against specifications before implementing shorter molding cycles on a routine production basis.

 

Typical Applications/End Uses: To come

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Technical Datasheet

UL 黄卡 2 •  E70062-249058

搜索 UL 黄卡 •  Ascend Performance Materials Operations LLC

•  Vydyne®

供货地区 • 北美洲 • 欧洲 • 亚太地区

添加剂 • 润滑剂

• 刚性，高 • 良好耐磨损性 • 韧性良好

• 高强度 • 耐化学性良好

特性 • 润滑

• 抗溶剂性 • 耐汽油性

• 脱模性能良好

• 快的成型周期 • 耐油性能

用途 • 衬套 • 工业应用 • 凸轮

• 电器外壳 • 连接器 • 轴承

机构评级 • ASTM D 4066 PA0111 • FDA 21 CFR 177.1500 • MIL M-20693B

• ASTM D 6779 PA0111 • FED L-P-410A

RoHS 合规性 • RoHS 合规

UL文件号 • E70062

外观 • 自然色

形式 • 粒子

加工方法 • 注射成型

物理性能 干燥 调节后的 单位制 测试方法

密度 1.14 -- g/cm³ ISO 1183

收缩率 ISO 294-4

垂直流动方向 : 23°C, 2.00 mm 2.0 -- %

流动方向 : 23°C, 2.00 mm 2.0 -- %

吸水率 ISO 62

23°C, 24 hr 1.2 -- %

平衡, 23°C, 50% RH 2.4 -- %

机械性能 干燥 调节后的 单位制 测试方法

拉伸模量 (23°C) 3300 1600 MPa ISO 527-2

拉伸应力 ISO 527-2

屈服, 23°C 88.0 55.0 MPa

断裂, 23°C 60.0 45.0 MPa

拉伸应变 (屈服, 23°C) 5.0 20 % ISO 527-2

标称拉伸断裂应变 (23°C) 20 > 50 % ISO 527-2

 

Vydyne® 21SPF

聚酰胺66

Ascend Performance Materials Operations LLC

机械性能 干燥 调节后的 单位制 测试方法

弯曲模量 (23°C) 3300 1050 MPa ISO 178

弯曲强度 (23°C) 105 30.0 MPa ISO 178

泊松比 0.40 -- ISO 527-2

冲击性能 干燥 调节后的 单位制 测试方法

简支梁缺口冲击强度 ISO 179/1eA

-30°C 5.0 7.0 kJ/m²

23°C 6.0 23 kJ/m²

简支梁无缺口冲击强度 ISO 179/1eU

-30°C 无断裂 无断裂

23°C 无断裂 无断裂

悬壁梁缺口冲击强度 ISO 180

-30°C 5.0 7.0 kJ/m²

23°C 6.0 23 kJ/m²

热性能 干燥 调节后的 单位制 测试方法

热变形温度

0.45 MPa, 未退火 210 -- °C ISO 75-2/B

1.8 MPa, 未退火 72.0 -- °C ISO 75-2/A

熔融温度 260 -- °C ISO 11357-3

线形热膨胀系数 ISO 11359-2

流动 : 23 到 55°C, 2.00 mm 1.0E-4 -- cm/cm/°C

横向 : 23 到 55°C, 2.00 mm 1.0E-4 -- cm/cm/°C

RTI Elec UL 746

0.400 mm 130 -- °C

0.710 mm 130 -- °C

1.50 mm 130 -- °C

3.00 mm 130 -- °C

RTI Imp UL 746

0.400 mm 75.0 -- °C

0.710 mm 75.0 -- °C

1.50 mm 75.0 -- °C

3.00 mm 75.0 -- °C

RTI UL 746

0.400 mm 75.0 -- °C

0.710 mm 85.0 -- °C

1.50 mm 85.0 -- °C

3.00 mm 85.0 -- °C

电气性能 干燥 调节后的 单位制 测试方法

体积电阻率 (0.750 mm) 1.0E+10 -- ohm•cm IEC 60093

介电强度 (1.00 mm) 26 -- kV/mm IEC 60243

耐电弧性 (3.00 mm) PLC 5 -- ASTM D495

漏电起痕指数 (3.00 mm) 600 -- V IEC 60112

高电弧燃烧指数(HAI) UL 746

0.710 mm PLC 0 --

1.50 mm PLC 0 --

3.00 mm PLC 0 --

高电压电弧起痕速率 (HVTR) PLC 0 -- UL 746

热丝引燃 (HWI) UL 746

0.710 mm PLC 4 --

1.50 mm PLC 3 --

3.00 mm PLC 3 --

 

Vydyne® 21SPF

聚酰胺66

Ascend Performance Materials Operations LLC

可燃性 干燥 调节后的 单位制 测试方法

UL 阻燃等级 UL 94

0.400 mm V-2 --

0.710 mm V-2 --

1.50 mm V-2 --

3.00 mm V-2 --

灼热丝易燃指数 IEC 60695-2-12

0.710 mm 800 -- °C

1.50 mm 800 -- °C

3.00 mm 930 -- °C

热灯丝点火温度 IEC 60695-2-13

0.710 mm 700 -- °C

1.50 mm 700 -- °C

3.00 mm 700 -- °C

极限氧指数 26 -- % ISO 4589-2

注射 干燥单位制

干燥温度 < 70.0°C

干燥时间 1.0 到 3.0hr

建议的最大回制料比例 50%

料筒后部温度 260 到 280°C

料筒中部温度 270 到 285°C

料筒前部温度 280 到 290°C

射嘴温度 280 到 300°C

加工（熔体）温度 285 到 300°C

模具温度 65.0 到 95.0°C

 

 

 

 

 

东莞市双帮塑胶原料有限公司大量销售塑料聚酰胺66  Ascend Performance Materials Operations LLC 尼龙66  美国首诺    尼龙66 Vydyne® 21SPF为塑料价格行情每天都有新的变化前天的报价不等于今天的报价。如果需要新的价格请电：13549213581，肖生。