FDA食品级，良好耐磨损性, 韧性良好, 高强度, 抗溶剂性, 衬套, 电器外壳, 连接器, 凸轮, 轴承

 

Vydyne® 21SPC1

聚酰胺66

Ascend Performance Materials Operations LLC

Technical Data

 

产品说明

 

Vydyne 21SPC1 is a general-purpose, improved-flow, lubricated PA66 resin available in natural color. 21SPC1 offers a balanced combination of properties characterized by high strength, rigidity, good toughness, a high melt point, abrasion resistance with good surface lubricity, and excellent resistance to many chemicals. Vydyne 21SPC1 resin has an external lubricant for improved machine feed and an internal lubricant for improved mold release.

 

Typical Applications/End Uses:

End uses for Vydyne 21SPC1 include terminal blocks, bearings, bushings, control cams, electrical connectors, housings, cable ties, fasteners, switch components and industrial parts that require chemical resistance, stiffness, wear resistance and rigidity.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Technical Datasheet

搜索 UL 黄卡 •  Ascend Performance Materials Operations LLC

•  Vydyne®

供货地区 • 北美洲 • 欧洲 • 亚太地区

添加剂 • 润滑剂

• 刚性，高 • 良好耐磨损性 • 韧性良好

特性 • 高强度 • 耐化学性良好 • 润滑

• 抗溶剂性 • 耐汽油性 • 通用

• 快的成型周期 • 耐油性能 • 脱模性能良好

用途 • 衬套 • 连接器 • 外壳

• 工业应用 • 凸轮 • 轴承

机构评级 • ASTM D 4066 PA0111 • FDA 21 CFR 177.1500 • MIL M-20693B

• ASTM D 6779 PA0111 • FED L-P-410A

RoHS 合规性 • RoHS 合规

UL文件号 • E70062

外观 • 自然色

形式 • 粒子

加工方法 • 注射成型

物理性能 干燥 调节后的 单位制 测试方法

密度 1.14 -- g/cm³ ISO 1183

收缩率 ISO 294-4

垂直流动方向 : 23°C, 2.00 mm 1.7 -- %

流动方向 : 23°C, 2.00 mm 1.8 -- %

吸水率 ISO 62

23°C, 24 hr 1.2 -- %

平衡, 23°C, 50% RH 2.4 -- %

机械性能 干燥 调节后的 单位制 测试方法

拉伸模量 (23°C) 3100 1400 MPa ISO 527-2

拉伸应力 ISO 527-2

屈服, 23°C 82.0 55.0 MPa

断裂, 23°C 55.0 45.0 MPa

拉伸应变 (屈服, 23°C) 5.0 25 % ISO 527-2

标称拉伸断裂应变 (23°C) 25 > 50 % ISO 527-2

弯曲模量 (23°C) 2900 1500 MPa ISO 178

弯曲强度 (23°C) 80.0 50.0 MPa ISO 178

泊松比 0.40 -- ISO 527

 

Vydyne® 21SPC1

聚酰胺66

Ascend Performance Materials Operations LLC

冲击性能 干燥 调节后的 单位制 测试方法

简支梁缺口冲击强度 ISO 179/1eA

-30°C 5.0 7.0 kJ/m²

23°C 6.0 20 kJ/m²

简支梁无缺口冲击强度 ISO 179/1eU

-30°C 无断裂 无断裂

23°C 无断裂 无断裂

悬壁梁缺口冲击强度 ISO 180

-30°C 5.0 7.0 kJ/m²

23°C 6.0 20 kJ/m²

热性能 干燥 调节后的 单位制 测试方法

热变形温度

0.45 MPa, 未退火 200 -- °C ISO 75-2/B

1.8 MPa, 未退火 70.0 -- °C ISO 75-2/A

熔融温度 260 -- °C ISO 11357-3

线形热膨胀系数 ISO 11359-2

流动 : 23 到 55°C 1.0E-4 -- cm/cm/°C

横向 : 23 到 55°C 1.0E-4 -- cm/cm/°C

RTI Elec UL 746

0.710 mm 130 -- °C

1.50 mm 130 -- °C

3.00 mm 130 -- °C

RTI Imp UL 746

0.710 mm 75.0 -- °C

1.50 mm 75.0 -- °C

3.00 mm 75.0 -- °C

RTI UL 746

0.710 mm 85.0 -- °C

1.50 mm 85.0 -- °C

3.00 mm 85.0 -- °C

电气性能 干燥 调节后的 单位制 测试方法

介电强度 (1.00 mm) 26 -- kV/mm IEC 60243

耐电弧性 (3.00 mm) PLC 5 -- ASTM D495

漏电起痕指数 (3.00 mm) 600 -- V IEC 60112

高电弧燃烧指数(HAI) UL 746

0.710 mm PLC 0 --

1.50 mm PLC 0 --

3.00 mm PLC 0 --

高电压电弧起痕速率 (HVTR) PLC 0 -- UL 746

热丝引燃 (HWI) UL 746

0.710 mm PLC 4 --

1.50 mm PLC 3 --

3.00 mm PLC 3 --

可燃性 干燥 调节后的 单位制 测试方法

UL 阻燃等级 UL 94

0.710 mm V-2 --

1.50 mm V-2 --

3.00 mm V-2 --

灼热丝易燃指数 IEC 60695-2-12

0.710 mm 800 -- °C

1.50 mm 800 -- °C

3.00 mm 930 -- °C

 

Vydyne® 21SPC1

聚酰胺66

Ascend Performance Materials Operations LLC

可燃性 干燥 调节后的 单位制 测试方法

热灯丝点火温度 IEC 60695-2-13

0.710 mm 700 -- °C

1.50 mm 700 -- °C

3.00 mm 700 -- °C

极限氧指数 25 -- % ISO 4589-2

注射 干燥单位制

干燥温度 < 70.0°C

干燥时间 1.0 到 3.0hr

建议的最大回制料比例 50%

料筒后部温度 260 到 280°C

料筒中部温度 270 到 285°C

料筒前部温度 280 到 290°C

射嘴温度 280 到 300°C

加工（熔体）温度 285 到 300°C

模具温度 65.0 到 95.0°C

 

 

 

 

 